1.1193, DIN CF45, AISI 1045
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.1193, DIN CF45, AISI 1045
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
CF45 | 626 | 1.1193 | CF45 | - | 1045 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.46 | 0.25 | 0.65 | - | - | - | - | - | - |
Description
CF45 is a medium carbon steel is used when greater strength and hardness is desired than in the "as rolled" condition. Extreme size accuracy, straightness and concentricity combine to minimize wear in high speed applications. Turned, ground and polished.
Applications
Used in gears, shafts, axles, bolts, studs, and machine parts.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 650-700oC, cool slowly. This will produce a maximum Brinell hardness of 207.
Normalizing
Temperature: 840-870oC.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 120-200oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 820-850oC followed by oil or water quenching. Hardness after quenching is 55-61 HRC.
Tempering
Tempering temperature: 550-660oC.
Forging
Hot forming temperature: 1100-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.1193 DIN CF45 AISI 1045 round bar 1.1193, DIN CF45, AISI 1045,forging 1.1193, DIN CF45, AISI 1045,1.1193, DIN CF45, AISI 1045 sheet,coil 1.1193, DIN CF45, AISI 1045,1.1193, DIN CF45, AISI 1045 flat bar,pipe 1.1193, DIN CF45, AISI 1045,1.1193, DIN CF45, AISI 1045 Lrregular
Prev:1.0605, DIN C75, AISI 1075
Next:1.1213, DIN Cf53, AISI 1055