50CrV4 1.8159 Spring Steel
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
50CrV4 1.8159 Spring Steel
50CrV4 is a tough oil quenching spring steel. When heat treated 50CrV4 offers good wear resistance. 50CrV4 is characterised by the addition of vanadium to the specification which differs 50CrV4 from standard spring steel specifications. |
TYPICAL ANALYSIS |
|
||
C. |
Mn. |
Cr. |
V. |
0.50% |
0.75% |
1.00% |
0.15% |
Forging:
Forge at 1050°C. Do not work this steel when it has fallen below 840°C.
Annealing:
Slow furnace cool from 840°/860°C.
Hardening:
Pre heat slowly to 650/700°C and thoroughly soak. Continue heating the 50CrV4 component to the final hardening temperature of 850/870°C and allow the component to be heated through. Quench in oil.
Tempering:
Temper the 50CrV4 tool immediately after quenching whilst tools are still hand warm. Re-heat to the tempering temperature, soak for one hour per 25 millimetre of total thickness, 2 hours minimum, then cool in air. For most 50CrV4 applications tempering will be between 400°/600°C.
Tempering °C |
100 |
200 |
300 |
400 |
450 |
500 |
550 |
600 |
HRc |
56 |
53 |
50 |
49 |
46 |
44 |
40 |
36 |
Mechanical properties
Heat treatment
Machining
Welding performance