1.7139, DIN 16MnCrS5, SAE 5117
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.7139, DIN 16MnCrS5, SAE 5117
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
16MNCRS5 | 779 | 1.7139 | 16MnCrS5 | - | SAE 5117 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.16 | max. 0.40 | 1.15 | 0.95 | - | - | - | - | - |
Description
Alloy special structural steels.
Applications
Component parts for steam boilers and turbines, shafts for higher temperature ranges.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Continuous Cooling Transformation (CCT) Diagram
Time-Temperature Transformation (TTT) Diagram
Soft Annealing
Heat to 650-700oC, cool slowly. This will produce a maximum Brinell hardness of 207.
Heat Treatment
Treatment | Temperature | Cooling |
Case hardening | 880-980oC | Oil (water), hot bath 160-250oC |
Carburising | 880-980oC | Salth bath (580-680oC), case hardening box |
Direct hardening | 880-980oC | Oil (water), hot bath 160-250oC |
Core refining | 860-900oC | Oil (water), hot bath 160-250oC |
Core refining | 780-820oC | Oil (water), hot bath 160-250oC |
Tempering
Tempering temperature: 150-200oC, air.
Hardness in Various Treated Conditions
Treated for stregth: 156-207 HB
Soft Annealed: 207 HB
Annealed to spherical carbides: max. 165 HB
Treated to pearlite structure: 140-187 HB
Distance From Quenched End in mm
mm | 1.5 | 3 | 5 | 7 | 9 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 |
H max. | 47 | 46 | 44 | 41 | 39 | 37 | 35 | 33 | 31 | 30 | 29 | 28 | 27 |
H min. | 39 | 36 | 31 | 28 | 24 | 21 | - | - | - | - | - | - | - |
HH max. | 47 | 46 | 44 | 41 | 39 | 37 | 35 | 33 | 31 | 30 | 29 | 28 | 27 |
HH min. | 42 | 39 | 35 | 32 | 29 | 26 | 24 | 22 | 20 | - | - | - | - |
HL max. | 44 | 43 | 40 | 37 | 34 | 32 | 30 | 28 | 26 | 25 | 24 | 23 | 22 |
HL min. | 39 | 36 | 31 | 28 | 24 | 21 | - | - | - | - | - | - | - |
Forging
Hot forming temperature: 1150-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.7139 DIN 16MnCrS5 SAE 5117 round bar 1.7139, DIN 16MnCrS5, SAE 5117,forging 1.7139, DIN 16MnCrS5, SAE 5117,1.7139, DIN 16MnCrS5, SAE 5117 sheet,coil 1.7139, DIN 16MnCrS5, SAE 5117,1.7139, DIN 16MnCrS5, SAE 5117 flat bar,pipe 1.7139, DIN 16MnCrS5, SAE 5117,1.7139, DIN 16MnCrS5, SAE 5117 Lrregular