1.6582, DIN 34CrNiMo6, AISI 4337/4340
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.6582, DIN 34CrNiMo6, AISI 4337/4340
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
VCNMO150 | 748 | 1.6582 | 34CrNiMo6 | 34CrNiMo6 | 4337/4340 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.34 | max.0.40 | 0.65 | 1.50 | 0.23 | 1.50 | - | - | - |
Description
VCNMO150 is a heat treatable, low steel/" target="_blank" class="keylink">alloy steel containing nickel, chromium and molybdenum. It is known for its toughness and capability of developing high strength in the heat treated condition while retaining good fatigue strength. A very popular, versatile steel. It can be heat-treated to produce a wide range of tensile strength in moderate sections.
Applications
Typical applications are for structural use, such as aircraft landing gear, power transmission gears and shafts and other structural parts, general engineering parts, hrough-hardened gears, connecting rods and bolts, gun barrels.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.84
Thermal conductivity [W/m.K]: 37.7
Specific heat capacity[J/g.K]: 0.46
Environmental resistance
Flammability: very good
Fresh water: good
Organic solvent: very good
Oxidation at 500oC: good
Sea water: average
Strong acid: poor
Strong alkalis: poor
Wear: very good
Weak acid: average
Weak alkalis: good
Minimum service temperature: -73.2 to -42.2oC
Maximum service temperature: 613-653oC
Continuous Cooling Transformation (CCT) Diagram.
Time-Temperature Transformation (TTT) Diagram
Normalizing
Normalizing temperature: 850-880oC.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 830-860oC followed by oil quenching. Qenching temperature in the end-quench test is 850oC.
Tempering
Tempering temperature: 540-660oC.
Mechanical Properties in Quenched and Tempered Condition
Diameter (mm) | 0.2 % proof stress (N/mm2) | Tensile strength (N/mm2) | Elongation (%) | Reduction of area (%) | Notch impact energy (ISO-V) (J) |
up to 16 | 980 | 1180-1380 | 9 | 40 | 41 |
17-40 | 885 | 1080-1280 | 10 | 45 | 48 |
41-100 | 785 | 980-1180 | 11 | 50 | 48 |
101-160 | 685 | 880-1080 | 12 | 55 | 48 |
161-250 | 590 | 780-930 | 13 | 55 | 48 |
Distance From Quenched End in mm
- | 1.5 | 3 | 5 | 7 | 9 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 | 45 | 50 |
H max. | 58 | 58 | 58 | 58 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 |
H min. | 50 | 50 | 50 | 50 | 49 | 48 | 48 | 48 | 48 | 47 | 47 | 47 | 46 | 45 | 44 |
HH max. | 58 | 58 | 58 | 58 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 | 57 |
HH min. | 53 | 53 | 53 | 53 | 52 | 51 | 51 | 51 | 51 | 50 | 50 | 50 | 50 | 49 | 48 |
HL max. | 55 | 55 | 55 | 55 | 54 | 54 | 54 | 54 | 54 | 54 | 54 | 54 | 53 | 53 | 53 |
HL min. | 55 | 55 | 55 | 55 | 54 | 54 | 54 | 54 | 54 | 54 | 54 | 54 | 54 | 53 | 53 |
Tempering Diagram
Hardenability Diagram
Forging
Hot forming temperature: 1100-900oC.
Machinability
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
Corrosion Resistance
This is a low steel/" target="_blank" class="keylink">alloy steel and not a corrosion resistant alloy. Protective coating should be used.
Welding
The alloy can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.
Cold working
The VCNMO150 alloy may be cold worked, in the annealed condition, by conventional methods and tooling. It has good ductility.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.6582 DIN 34CrNiMo6 AISI 4337/4340 round bar 1.6582, DIN 34CrNiMo6, AISI 4337/4340,forging 1.6582, DIN 34CrNiMo6, AISI 4337/4340,1.6582, DIN 34CrNiMo6, AISI 4337/4340 sheet,coil 1.6582, DIN 34CrNiMo6, AISI 4337/4340,1.6582, DIN 34CrNiMo6, AISI 4337/4340 flat bar,pipe 1.6582, DIN 34CrNiMo6, AISI 4337/4340,1.6582, DIN 34CrNiMo6, AISI 4337/4340 Lrregular