- 1.2826, DIN 60MnSiCr4 round bar
- 1.2826, DIN 60MnSiCr4 forging
- 1.2826, DIN 60MnSiCr4 sheet
- 1.2826, DIN 60MnSiCr4 flat bar
- 1.2826, DIN 60MnSiCr4 pipe
1.2826, DIN 60MnSiCr4
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2826, DIN 60MnSiCr4
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
VZ197 | 197 | 1.2826 | 60MnSiCr4 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.62 | 0.90 | 1.00 | 0.30 | - | - | - | - | - |
Description
VZ197 is a heat treatable, low steel/" target="_blank" class="keylink">alloy steel containing manganese, silicon and chromium.
Applications
Dies and lower dies, tri mming tools, hammer and pressing saddles.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.78
Continuous Cooling Transformation (CCT) Diagram
Soft Annealing
Heat to 680-720oC, cool slowly. This will produce a maximum Brinell hardness of 240.
Hardening
Harden from a temperature of 820-860oC followed by oil quenching or hot quenching at 180-220oC.
Tempering
Tempering temperature: 300-550oC.
Forging
Hot forming temperature: 1050-850oC.
Machinability
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
Corrosion Resistance
This is a low steel/" target="_blank" class="keylink">alloy steel and not a corrosion resistant alloy. Protective coating should be used.
Welding
The alloy can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.2826 DIN 60MnSiCr4 round bar 1.2826, DIN 60MnSiCr4,forging 1.2826, DIN 60MnSiCr4,1.2826, DIN 60MnSiCr4 sheet,coil 1.2826, DIN 60MnSiCr4,1.2826, DIN 60MnSiCr4 flat bar,pipe 1.2826, DIN 60MnSiCr4,1.2826, DIN 60MnSiCr4 Lrregular
Prev:1.5223, DIN 42MnV7
Next:1.7701, DIN 51CrMoV4, AISI 4150