Ti-2.5Cu
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Ti-2.5Cu Ti Alloy Steel
Titanium IMI 230 (Ti-2.5Cu)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes: Annealed; Aging increases Strength
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 4.56 g/cc | 0.165 lb/in³ | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Ultimate | 620 MPa | 89900 psi | |
Tensile Strength, Yield | 480 MPa | 69600 psi | |
Elongation at Break | 24.0 % | 24.0 % | |
Modulus of Elasticity | 105 GPa | 15200 ksi | |
Poissons Ratio | 0.310 | 0.310 | Typical for alpha titanium alloy. |
Fatigue Strength |
280 MPa @# of Cycles 1.00e+7 |
40600 psi @# of Cycles 1.00e+7 |
|
Shear Modulus | 40.1 GPa | 5820 ksi | Calculated from typical values. |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 0.0000650 ohm-cm | 0.0000650 ohm-cm | |
Thermal Properties | Metric | English | Comments |
CTE, linear |
9.02 µm/m-°C @Temperature 20.0 - 100 °C |
5.01 µin/in-°F @Temperature 68.0 - 212 °F |
|
9.10 µm/m-°C @Temperature 20.0 - 300 °C |
5.06 µin/in-°F @Temperature 68.0 - 572 °F |
average | |
9.46 µm/m-°C @Temperature 20.0 - 600 °C |
5.26 µin/in-°F @Temperature 68.0 - 1110 °F |
average | |
Specific Heat Capacity | 0.525 J/g-°C | 0.125 BTU/lb-°F | Typical value for titanium alloys. |
Thermal Conductivity | 13.0 W/m-K | 90.2 BTU-in/hr-ft²-°F | |
Beta Transus | 895 °C | 1640 °F | |
Component Elements Properties | Metric | English | Comments |
Carbon, C | <= 0.0800 % | <= 0.0800 % | |
Copper, Cu | 2.00 - 3.00 % | 2.00 - 3.00 % | |
Hydrogen, H | <= 0.0100 % | <= 0.0100 % | |
Iron, Fe | <= 0.200 % | <= 0.200 % | |
Nitrogen, N | <= 0.0500 % | <= 0.0500 % | |
Other, total | <= 0.400 % | <= 0.400 % | |
Oxygen, O | <= 0.200 % | <= 0.200 % | |
Titanium, Ti | 96.06 - 98.0 % | 96.06 - 98.0 % | As Balance; Elemental Compostions per ASTM B265 |
Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium IMI 230 (Ti-2.5Cu), aged
Titanium Ti-5Al-2.5Sn (Grade 6)
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)
MTA231 / 14121
Mechanical properties
Heat treatment
Machining
Welding performance