Home > Standard > 1.4057, DIN X17CrNi16-2, AISI 431 standard

1.4057, DIN X17CrNi16-2, AISI 431

1.4057, DIN X17CrNi16-2, AISI 431 standard Download, We provide the main countries around the ISO standard download, including: AISI(US),UNS(US),SAE(US),ASTM(US),AMS(US),ASME(US),MIL(US),FED(US),DIN(DEU),JIS(JPN),AFNOR(FR),B.S.(UK),SS(SWE),UNI(ITA).

Production specification

Round bar standard Download
Square-shape steel standard Download
Plate steel standard Download
Billet standard Download
Flat bar standard Download
wire standard Download
tube standard Download
pipe standard Download
Forging standard Download
casting standard Download
sheet standard Download
round bar standard Download
coil standard Download
Bar stock standard Download
profiled bar standard Download

1.4057, DIN X17CrNi16-2, AISI 431

Designation by Standards

 

Brand Name LH No. Mat. No. DIN EN AISI
PK2SP 911 1.4057 X17CrNi16-2 X17CrNi16-2 431



Chemical Composition (in weight %)

C Si Mn Cr Mo Ni V W Others
0.17 max. 1.0 max. 1.50 16.00 - 2.00 - - -



Description
431 is a martensitic stainless combining excellent impact strength at high hardness levels with the best corrosion resistance of any martensitic stainless steels. Steel with high polishability. For application up to working temperature 500oC.

Applications
431 has been successfully used in a variety of aircraft and general industrial applications. These include fasteners, shafts, bolts, valve components and chemical equipment, components for dairies, machine building and paper industry.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 216
Density [g/cm3]: 7.70
Thermal conductivity [W/m.K]: 25.0
Electric resistivity [Ohm mm2/m]: 0.70
Specific heat capacity[J/g.K]: 0.46

Modulus of Elasticity [103 N/mm2]

20oC 200oC 400oC
216 205 190



Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC 20-200oC 20-300oC 20-400oC 20-500oC 20-600oC 20-700oC
11.2 11.5 11.7 11.9 12.0 12.1 12.0




Soft Annealing
Heat to 660-750oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 295.

Hardening
Harden from a temperature of 980-1030oC followed by oil or air quenching. Hardness after quenching is about 47 HRC.

Tempering
Tempering temperature: For Q+T 800: 750-800oC. For Q+T 900: 600-650oC.

0.2 % Proof Stress (N/mm2) at Elevated Temperatures

Condition 100oC 150oC 200oC 250oC 300oC 350oC 400oC
Q+T 800 515 495 475 460 440 405 355
Q+T 900 565 525 505 490 470 430 375


Forging
Hot forming temperature: 1100-800oC, slow cooling.

Machinability
In the fully annealed condition, 431 will gall and build up on the tools. Good surface finishes are not easily obtained.

Corrosion Resistance
431 is superior to all other martensitic grades in terms of corrosion resistance. Will resist dilute acids and alkalis, neutral and basic salts, food acids, fresh water and atmosphere.

Welding
Most electric welding procedures have proven successful with 431 stainless. Filler metal should be AWS E/ER410.To avoid cracking, pre-heat the workpiece to 204-316oC. After air cooling, treat at 649oC to reattain maximum properties.

Embittlemnt: It must be in mind that the temperature range between 425 and 525oC must be avoided owing to embritllement at 475oC.

Cold working
This alloy is easily drawn, spun, headed, sheared and bent compared with other stainless steels.

Related hot word search:1.4057 DIN X17CrNi16-2 AISI 431 1.4057, DIN X17CrNi16-2, AISI 431 round bar,1.4057, DIN X17CrNi16-2, AISI 431 forging,1.4057, DIN X17CrNi16-2, AISI 431 sheet,1.4057, DIN X17CrNi16-2, AISI 431 coil,1.4057, DIN X17CrNi16-2, AISI 431 flat bar,1.4057, DIN X17CrNi16-2, AISI 431 pipe,1.4057, DIN X17CrNi16-2, AISI 431 Lrregular