P20 Tool Steel

P20 Tool Steel

P20 is a pre hardened high tensile steel/" target="_blank" class="keylink">tool steel which offers ready machineability in the hardened and tempered condition, therefore does not require further heat treatment . This eliminates the risks, cost, and waiting time of heat treatment thus avoiding the associated possibility of distortion or even cracking. Subsequent component modifications can easily be carried out. 

Forging:
Heat slowly and uniformly to 1050°C. Do not forge below 930°C. After forging cool slowly.

Annealing:
P20 should always be annealed after forging and before rehardening. Heat uniformly to 770/790°C. Soak well and cool slowly in the furnace.

Hardening:
Heat uniformly to 840/870°C until heated through. Quench in oil.

Tempering:
Heat uniformly and thoroughly at the selected tempering temperatures and hold at heat for one hour per 25 millimetre of total thickness.

Nitriding:
Moulds machined from pre hardened P20 may be nitrided to give a hard surface which is very resistant to wear and erosion. A nitrided surface also increases the corrosion resistance. The surface hardness after nitriding at a temperature of 525°C in ammonia gas will be approximately 650HV.

Tufftriding:
Tufftriding at 570°C will give a surface hardness of approximately 700HV. After 2 hours treatment the hard layer will be approximately 0.01mm

Flame & Induction Hardening:
P20 can be flame or induction hardened to a hardenss of 50 to 55 HRc. Cooling in air is preferable. Smaller pieces may however require forced cooling. Hardening should be immediately followed by tempering.

Hard Chromium Plating:
After hard chromium plating the steel should be tempered for approximately 4 hours at 180°C, in order to avoid hydrogen embrittlement.

Case Hardening:
In order to maintain maximum surface hardness P20 may be case hardened. Before case hardening is carried out the steel should be annealed. To carburise, pack with carburising powder into a cast iron or heat resisting steel box and see that the articles are separated from the sides by at least two inches of carburising powder. Lute the lid with fireclay. Heat to the carburising temperature of 880°C and soak for sufficient time to give the required depth of case. Cool to 800/820°C and quench in oil. Tempering will then be necessary. Reheat to 200/300°C and allow to cool in the air to give a final  surface hardness of Rockwell C55/59

Welding:
Firstly heat to approximately 400 to 500°C. Weld at approximately 400 to 500°C and stress relieve. Use Chromium-Nickel-Molybdenum alloyed basic electrodes for welding of structural steels. Welding may also be carried out using an austenitic stainless steel electrode. In this case the stipulated increased working temperature may be modified, but the weld metal has a lower strength than the parent material.