1.2376, DIN X96CrMoV12
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2376, DIN X96CrMoV12
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
CRV1 | 831 | 1.2376 | X96CrMoV12 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.96 | 0.30 | 0.30 | 11.50 | 0.90 | - | 0.90 | - | - |
Description
Chromium cold work steel/" target="_blank" class="keylink">tool steel with high durability and cutting performance for very tough items.
Applications
Wear resisting tools, pressure die casting tools, pressing tools for light and heavy metals. This steel grade can be water cooled.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.72
Continuous Cooling Transformation (CCT) Diagram.
Soft Annealing
Heat to 820-850oC, cool slowly. This will produce a maximum Brinell hardness of 250.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 1030-1060oC followed by oil quenching or warm bath quenching 350-450oC. Hardness after quenching is 62-63 HRC.
Tempering
Tempering temperature: See the data bellow.
Tempering Diagram
Forging
Hot forming temperature: 1050-900oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance