1.2747, DIN X210Cr12, AISI D3
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2747, DIN X210Cr12, AISI D3
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
TMCN1 | 822 | 1.2747 | X210Cr12 | - | D3 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
2.05 | 0.25 | 0.30 | 11.50 | - | - | - | - | - |
Description
TMCN1 is Ni-Cr steel with added Mo and V and good thoughness and resistance to temperature changes.
Applications
Pilger mandrels up to diameter 140 -200 mm.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 620-680oC, cool slowly.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 840-870oC followed by oil or air quenching.
Tempering
Tempering temperature: 620-670oC.
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.2747 DIN X210Cr12 AISI D3 round bar 1.2747, DIN X210Cr12, AISI D3,forging 1.2747, DIN X210Cr12, AISI D3,1.2747, DIN X210Cr12, AISI D3 sheet,coil 1.2747, DIN X210Cr12, AISI D3,1.2747, DIN X210Cr12, AISI D3 flat bar,pipe 1.2747, DIN X210Cr12, AISI D3,1.2747, DIN X210Cr12, AISI D3 Lrregular