1.2564, DIN X30WCrV41
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2564, DIN X30WCrV41
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
UTOP1 | 856 | 1.2564 | X30WCrV41 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.30 | 0.95 | 0.40 | 1.05 | - | - | 0.18 | 3.75 | - |
Description
Tungsten-chromium hot work steel suitable for water cooling.
Applications
Water cooled dummy blocks for the extrusion of copper and copper alloys, hand casting chills for copper alloys.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 820-840oC, cool slowly in furnace. Holding time 4-6 hours. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by slow cooling. Time is 1-2 hours. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 960-1050oC followed by water or oil quenching. Hardness after quenching is appr. 52 HRC (water quenching), 47 HRC (oil quenching).
Tempering
Tempering temperature: 560-700oC.
Nitriding
Possible. Preheating before use: 200-300 oC, absolutely necessary.
Tempering Diagram
Forging
Hot forming temperature: 1100-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance