DIN C80W1
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
DIN C80W1
Designation by Standards
Brand Name | Ravne No. | Mat. No. | DIN | EN | AISI |
KOSE | 650 | - | C80W1 | - | 108 |
Chemical Composition (in weight %)
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.80 | max. 0.20 | 0.20 | - | - | - | - | - | - |
Description
Low alloyed cold work steel/" target="_blank" class="keylink">tool steel.
Applications
Tools for wood and soft metals.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 680-720oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 175.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 780-810oC followed by oil quenching. Hardness after quenching is 64 HRC.
Tempering
Tempering temperature: 350-450oC. Hardness after tempering is 50-52 HRC.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 200oC | 300oC | 400oC | 450oC |
67 | 64 | 54 | 45 | 41.5 |
Tempering Diagram
Forging
Hot forming temperature: 1050-800oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance