- 1.2833, DIN 100V1, AISI W2 round bar
- 1.2833, DIN 100V1, AISI W2 forging
- 1.2833, DIN 100V1, AISI W2 sheet
- 1.2833, DIN 100V1, AISI W2 flat bar
- 1.2833, DIN 100V1, AISI W2 pipe
1.2833, DIN 100V1, AISI W2
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2833, DIN 100V1, AISI W2
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
OC100ES | 651 | 1.2833 | 100V1 | - | W2 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
1.05 | 0.20 | 0.25 | - | - | - | 0.15 | - | - |
Description
Low alloyed water-hardening steel/" target="_blank" class="keylink">tool steel.
Applications
Cold working tools for steels and metals when hard surface and tough core are demand; tap drills, dies, broaching tools, stone working tools.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 190-210
Density [g/cm3]: 7.85
Thermal conductivity [W/m.K]: 14.4
Electric resistivity [Ohm mm2/m]: 0.20
Specific heat capacity[J/g.K]: 0.46
Soft Annealing
Heat to 680-720oC, cool slowly. This will produce a maximum Brinell hardness of 213.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 600-650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 760-800oC followed by water quenching. Hardness after quenching is 65 HRC.
Tempering
Tempering temperature: 100-200oC.
Forging
Hot forming temperature: 1000-800oC.
Machinability
No data.
Corrosion Resistance
Corrosion resistance of this alloy is better than that of plain carbon steels. However it will rust unless given protective treatment.
Mechanical properties
Heat treatment
Machining
Welding performance