AISI S5
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
AISI S5
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
OH237 | 237 | - | - | - | S5 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.57 | 2.00 | 0.80 | 0.30 | 0.78 | - | 0.25 | - | - |
Description
Cold work steel/" target="_blank" class="keylink">tool steel. Shock resisting steel/" target="_blank" class="keylink">tool steel with good toughness at high strength levels.
Applications
Different cutting parts, chisels, rivet sets, punches, driver bits.
Physical properties (avarage values) at ambient temperature
Density [g/cm3]: 7.74
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC | 20-700oC |
13.1 | 13.7 | 14.4 | 14.4 | 14.7 | 14.9 | 15.0 |
Continuous Cooling Transformation (CCT) Diagram
Time-Temperature Transformation (TTT) Diagram
Click the image to enlarge the diagram.
Soft Annealing
Heat to 770-800oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 880-920oC followed by oil quenching. Hardness after quenching is 63 HRC.
Tempering
Tempering temperature: See the data bellow.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 200oC | 300oC | 400oC | 500oC | 550oC |
62 | 60 | 58 | 56 | 50 | 48 |
Tempering Diagram
Forging
Hot forming temperature: 1050-900oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance