1.2604, DIN 73WCrMoV2-2
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2604, DIN 73WCrMoV2-2
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
Steel OH248 | 248 | 1.2604 | 73WCrMoV2-2 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.73 | 0.30 | 0.50 | 0.50 | 0.33 | - | 0.23 | 0.55 | - |
Description
Low alloyed cold working steel/" target="_blank" class="keylink">tool steel.
Applications
Tap drills, broaching tools, milling cutters and other cutting tools. It is usually supplied as silver steel.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Continuous Cooling Transformation (CCT) Diagram
Time-Temperature Transformation (TTT) Diagram
Soft Annealing
Heat to 680-710oC, cool slowly. This will produce a maximum Brinell hardness of 225.
Hardening
Harden from a temperature of 810-840oC followed by oil quenching.Hardness after quenching is 63 HRC.
Tempering
Tempering temperature: 180-300oC.
Forging
Hot forming temperature: 1050-900oC.
Machinability
The machinability rating of D3 is roughly 25 % that of free machining carbon steel 1018. Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding.
Mechanical properties
Heat treatment
Machining
Welding performance