- 1.2562, DIN 142W13 round bar
- 1.2562, DIN 142W13 forging
- 1.2562, DIN 142W13 sheet
- 1.2562, DIN 142W13 flat bar
- 1.2562, DIN 142W13 pipe
1.2562, DIN 142W13
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2562, DIN 142W13
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
OW5 | 832 | 1.2562 | 142W13 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
1.43 | 0.23 | 0.30 | 0.35 | - | - | 0.25 | 3.05 | - |
Description
Low alloyed W cold working steel/" target="_blank" class="keylink">tool steel.
Applications
Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 8.0
Soft Annealing
Heat to 720-750oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 270.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 800-830oC followed by water quenching. Hardness after quenching is 66 HRC.
Tempering
Tempering temperature: 100-250oC.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 150oC | 200oC | 250oC | 300oC |
66 | 65 | 64 | 62 | 60 |
Tempering Diagram
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance