- 1.3265, DIN S18-1-2-10, AISI T5 round bar
- 1.3265, DIN S18-1-2-10, AISI T5 forging
- 1.3265, DIN S18-1-2-10, AISI T5 sheet
- 1.3265, DIN S18-1-2-10, AISI T5 flat bar
- 1.3265, DIN S18-1-2-10, AISI T5 pipe
1.3265, DIN S18-1-2-10, AISI T5
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.3265, DIN S18-1-2-10, AISI T5
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
BRC3 | 880 | 1.3265 | S18-1-2-10 | HS18-0-1-10 | T5 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.76 | max. 0.45 | max. 0.40 | 4.15 | 0.65 | - | 1.55 | 18.00 | Co: 9.50 |
Description
This alloy is a High Speed, tungsten type steel/" target="_blank" class="keylink">tool steel. It is a deep hardening steel.
Applications
Generally used as cutting tools, broaches and cold extrusion punches, turning blades, punchers, metal working blades.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 217
Density [g/cm3]: 8.70
Thermal conductivity [W/m.K]: 19.0
Electric resistivity [Ohm mm2/m]: 0.65
Specific heat capacity[J/g.K]: 0.46
Soft Annealing
Heat to 800-830oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 300.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Hard4en from a temperature of 1250-1280oC followed by salt bath or thermal quenching or warm bath approx. 550oC.
Tempering
Tempering temperature: 550-590oC.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 150oC | 200oC | 250oC | 300oC | 350oC | 400oC | 450oC | 500oC | 550oC | 600oC | 650oC |
64.0 | 64.5 | 63.0 | 62.5 | 62.0 | 62.0 | 62.5 | 63.6 | 64.8 | 66.0 | 64.0 | 60.0 |
Forging
Hot forming temperature: 1150-900oC.
Machinability
Machinability of T5 is only fair. It ranks as 50% that of the W group water hardening simple steel/" target="_blank" class="keylink">tool steels.
Corrosion Resistance
Corrosion resistance of this alloy is better than that of plain carbon steels. However it will rust unless given protective treatment.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.3265 DIN S18-1-2-10 AISI T5 round bar 1.3265, DIN S18-1-2-10, AISI T5,forging 1.3265, DIN S18-1-2-10, AISI T5,1.3265, DIN S18-1-2-10, AISI T5 sheet,coil 1.3265, DIN S18-1-2-10, AISI T5,1.3265, DIN S18-1-2-10, AISI T5 flat bar,pipe 1.3265, DIN S18-1-2-10, AISI T5,1.3265, DIN S18-1-2-10, AISI T5 Lrregular