11.3343, DIN S5-5-2, AISI M2
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
11.3343, DIN S5-5-2, AISI M2 Tool Steel
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
BRM2 | 876 | 1.3343 | S5-5-2 | HS6-5-2 | M2 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.90 | max. 0.45 | max. 0.40 | 4.15 | 4.95 | - | 1.90 | 6.60 | - |
Description
M2 is a higher carbon version of the M1 steel/" target="_blank" class="keylink">tool steel (Molybdenum High Speed Tool Steel). The M2 alloy has somewhat better wear resistance than M1. Very high resistance to softening at elevated temperatures. Very high resistance to wear. Good toughness and cutting capability. Deep hardening resposnse.
Applications
Primarily used for cutting tools, knives, tap and spiral drills, broaching tools, milling cutters, woodworking tools, cold work tools.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 217
Density [g/cm3]: 8.12
Thermal conductivity [W/m.K]: 19.0
Electric resistivity [Ohm mm2/m]: 0.54
Specific heat capacity[J/g.K]: 0.46
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC | 20-700oC | 20-800oC |
10.7 | 11.7 | 11.9 | 12.4 | 12.7 | 13.1 | 13.4 | 13.4 |
Soft Annealing
Heat to 820-880oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 225-280.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Heat up to 450-600oC, then preheat to 850oC, and to 1050oC. Harden from a temperature of 1180-1230oC followed by oil, air quenching or warm bath 550oC. Hardness after quenching is min. 64 HRC.
Tempering
Tempering temperature: 3 x 1 hour at 540-560oC.
Tempering Temperature (oC) vs. Hardness (HRC)
200oC | 300oC | 400oC | 500oC | 525oC | 550oC | 575oC | 600oC | 650oC | 700oC |
63 | 61 | 61 | 62.5 | 64 | 65 | 64 | 62.5 | 57 | 47 |
Forging
Hot forming temperature: 1120-926oC.
Machinability
M2 is classified as a "medium" machinability steel/" target="_blank" class="keylink">tool steel in the annealed condition. It may be shaped by grinding but is relatively poor in regard to capability of being ground. Its machinability rating is 50% as compared to the W group water hardening steel/" target="_blank" class="keylink">tool steel.
Corrosion Resistance
Not normally employed in applications requiring corrosion resistance.
Welding
Consult the alloy supplier for information on the advisability of welding.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:11.3343 DIN S5-5-2 AISI M2 Tool Steel round bar 11.3343, DIN S5-5-2, AISI M2,forging 11.3343, DIN S5-5-2, AISI M2,11.3343, DIN S5-5-2, AISI M2 sheet,coil 11.3343, DIN S5-5-2, AISI M2,11.3343, DIN S5-5-2, AISI M2 flat bar,pipe 11.3343, DIN S5-5-2, AISI M2,11.3343, DIN S5-5-2, AISI M2 Lrregular