1.1140, DIN Cm15, AISI 1015
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.1140, DIN Cm15, AISI 1015
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
CM15 | 606 | 1.1140 | Cm15 | - | 1015 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.15 | max.0.40 | 0.45 | - | - | - | - | - | S=0.020-0.040% |
Description
CM15 is a plain carbon steel with a nominal 0.15% carbon content and higher content of S (0.020-0.040%).
Applications
Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and steel/" target="_blank" class="keylink">alloy steel tubes. Steels for case hardening.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 650-700oC, cool slowly in furnace.
Carburizing
Carburizing temperature: 880-980oC.
Cooling from carburizing temperature: water, oil, air, thermal bath.
Core hardening temperature: 880-920oC.
Tempering
Tempering temperature: 150-180oC.
Forging
Hot forming temperature: 1050-850oC.
Machinability
Machinability of CM15 steel is fairly good, especially in the cold drawn or cold worked condition. Based upon carbon steel AISI 1112 as a reference that is considered 100% machinable (easily machined) the CM15 steel has a rating of 55%.
Mechanical properties
Heat treatment
Machining
Welding performance