1.2550 60WCrV7 Tool Steel
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2550 60WCrV7 Tool Steel
1.2550 60WCrV7 is a high duty shock resisting alloy steel/" target="_blank" class="keylink">tool steel. In the hardened condition 1.2550 60WCrV7 is a heat resisting tool steel that combines great hardness with good toughness and shock resisting properties. |
TYPICAL ANALYSIS |
|
|
||
C. |
Si. |
Mn. |
Cr. |
V. |
0.50% |
0.80% |
1.50% |
2.50% |
0.20% |
Forging:
Heat the 1.2550 steel/" target="_blank" class="keylink">tool steel component slowly and uniformly to 1000°C. Forge within a range of 1000/800°C, reheating if necessary. Cool slowly (preferably in a furnace) to avoid setting up stresses.
Annealing:
Heat the 1.2550 tool uniformly to 770°C, equalise, then furnace cool.
Stress Relieving:
If machining operations have been heavy or if the 1.2550 tool has an unbalanced section, remove stresses before hardening by heating up to 700°C, equalise, then cool slowly.
Hardening:
Pre heat the 1.2550 steel/" target="_blank" class="keylink">tool steel to 650°C and thoroughly soak. Continue heating to the final hardening temperature of 900/950°C. Allow sufficient time for the component to be heated through. Quench in oil.
Martempering:
Martempering is an alternative hardening procedure for 1.2550 which may be used when suitable salt bath equipment is available.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperature and hold for at least one hour per inch of total thickness.
Tempering °C |
150 |
200 |
250 |
350 |
400 |
HRc |
62/61 |
61/60 |
60/59 |
58/57 |
55/54 |
Mechanical properties
Heat treatment
Machining
Welding performance