1.2344 X40CrMoV5-1 Tool Steel
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2344 X40CrMoV5-1 is an air hardening hot work steel/" target="_blank" class="keylink">tool steel which combines a |
TYPICAL ANALYSIS |
|
|
|||
C. |
Si. |
Mn. |
Cr. |
Mo. |
V. |
0.38% |
1.00% |
0.40 |
5.00% |
1.30% |
1.00% |
Forging:
Heat slowly and uniformly to 700°C. Forge 1.2344 within a range of 1050/1150°C reheating if necessary, since forging must not be carried out below 850°C. Cool slowly, preferably in a furnace since this is an air hardening steel.
Annealing:
Heat uniformly to 750/800°C, soak thoroughly and furnace cool.
Stress Relieving:
After rough machining the 1.2344 components must be stress relieved, heat to 650/700°C and hold for 2 hours then furnace cool.
Hardening:
Pre heat the 1.2344 to 750/850°C and soak thoroughly, then increase rapidly to the hardening temperature of 1000/1030°C in a controlled atmosphere or neutral salt bath. Cool in air.
This steel is suitable for vacuum hardening.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperature, depending on the hardness requirement. Hold for at least two hours per inch of total thickness and cool in air. Double tempering of 1.2344 is strongly recommended.
Tempering °C |
400 |
500 |
550 |
600 |
650 |
HRc |
54 |
56 |
54 |
49 |
47 |
Tufftriding:
Tufftriding 1.2344 hot work steel/" target="_blank" class="keylink">tool steel is done in a special salt bath at 570°C. Holding time 2 hours. It gives a surface hardness of approximately 950-1000HV.
Nitriding:
Nitriding 1.2344 hot work steel/" target="_blank" class="keylink">tool steel gives a hard surface case which is very resistant to wear and erosion and also increases the corrosion resistance. Nitriding in ammoniac gas at 525°C gives a surface hardness of approximately 1000HV 1250HV. Before nitriding, the tool should be hardened and tempered at approximately 50°C above nitriding temperature.
Temperature |
Time |
Approximate Depth of Case |
525°C |
10 hours |
0.125mm |
525°C |
20 hours |
0.180mm |
525°C |
40 hours |
0.250mm |
525°C |
60 hours |
0.300mm |
Welding:
Due to the high risk of crack formation welding of 1.2344 steel/" target="_blank" class="keylink">tool steel should be avoided, if possible. When, howe ver welding is essential, the following serves as a guide:
A . Welding of soft annealed 1.2344 X40CrMoV5 steel/" target="_blank" class="keylink">tool steel
· Preheat to 300 - 500°C
· Weld at 300-500°C
· Immediately stress relieve at 675-750°C. Soaking time at temperature, 3 hours.
Electrode: Cr-Mo alloy electrode for welding low alloyed steel.
B. Welding in connection with hardening of soft annealed 1.2344 X40CrMoV5 steel/" target="_blank" class="keylink">tool steel.
· Heat to austenitizing temperature.
· Cool to approx. 500°C
· Weld at approx. 500°C
· Cool to approx. 100°C in the same way as at normal hardening, then temper to desired hardness.
Electrode: Hard facing electrode.
C. Repair welding of 1.2344 X40CrMoV5 steel/" target="_blank" class="keylink">tool steel in hardened and tempered condition.
· Preheat to the tempering temperature (min. 300°C) previously used.
· Weld at tempering temperature. Do not weld below 150°C.
· Reheat immediately to 300°C. Soaking time 3 hours.
· Cool in air to approx. 80°C.
· Reheat immediately to 300°C. Soaking time 3 hours.
Electrode: Hard facing electrode.
Physical Properties: 1.2344 X40CrMoV5 | Temperature: | ||
200°C | 400°C | 600°C | |
Density (Kg/dm³) | 7.75 | 7.70 | 7.65 |
Coefficient of thermal expansion (per °C from 0°C) | 11.9 x 10-6 | 12.4 x 10-6 | 12.8 x 10-6 |
Thermal conductivity (cal/cm.s °C) | 60.0 x 10-3 | 62.4 x 10-3 | 63.6 x 10-3 |
Modulus of elasticity: | |||
N/mm² | 184 000 | 175 000 | 154 000 |
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.2344 X40CrMoV5-1 Tool Steel round bar 1.2344 X40CrMoV5-1 Tool Steel,forging 1.2344 X40CrMoV5-1 Tool Steel,1.2344 X40CrMoV5-1 Tool Steel sheet,coil 1.2344 X40CrMoV5-1 Tool Steel,1.2344 X40CrMoV5-1 Tool Steel flat bar,pipe 1.2344 X40CrMoV5-1 Tool Steel,1.2344 X40CrMoV5-1 Tool Steel Lrregular