1.2363 X100CrMoV5-1 Tool Steel
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2363 X100CrMoV5-1 Tool Steel
1.2363 X100CrMoV5-01 is a air hardening cold work steel/" target="_blank" class="keylink">tool steel, which offers high surface hardness after heat treatment, good wear resistance, great through hardenability. 1.2363 X100CrMoV5-01 steel/" target="_blank" class="keylink">tool steel is also characterised by its high dimensional stability after heat treatment, high compression resistance and good resistance to tempering. |
Typical Analysis 1.2363 X100CrMoV5-01 | ||||
C. |
Mn. |
Cr. |
W. |
V. |
0.95% |
1.25% |
0.50% |
0.50% |
0.20% |
Forging:
Heat slowly and uniformly to 700°C. Forge within a range of 1050/1100°C, reheating if necessary. Cool very slowly (preferably in a furnace) to avoid setting up stresses.
Annealing:
Heat uniformly to 850°C, equalise, then furnace cool. (Hardness about 215 Brinell). Fully machined 1.2363 components should be packed during annealing.
Stress Relieving:
If machining operations have been heavy or if the 1.2363 component has an unbalanced section, remove stresses before hardening by heating up to 675°C, equalise, then cool in furnace to 500°C before slowly cooling in air.
Hardening:
Pre heat to 600/700°C and thoroughly soak. Continue heating to the final hardening temperature of 950/980°C. Allow sufficient time for the 1.2363 tool to be heated through. Quench in oil or cool in air.
Martempering:
Martempering is an alternative hardening procedure which may be used when suitable salt bath equipment is available.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperatures and hold for at least one hour per inch of total thickness.
Tempering °C |
150 |
200 |
250 |
300 |
350 |
400 |
HRc |
62/61 |
61/60 |
60/59 |
659/580 |
58/57 |
58/57 |
Hard Chromium Plating:
After hard chromium plating tempering of 1.2363 steel/" target="_blank" class="keylink">tool steel is recommended at 180°C for 4 hours to avoid hydrogen embrittlement. Tempering is to be performed immediately after chromium plating.
Welding:
Due to the high risk of crack formation welding of 1.2363 steel/" target="_blank" class="keylink">tool steel should be avoided, if possible. When, howe ver welding is essential, the following serves as a guide:
A. Welding of soft annealed 1.2363 steel/" target="_blank" class="keylink">tool steel
· Preheat to 300 - 500°C.
· Weld at 300-500°C.
· Immediately stress relieve.
Electrode: Cr-Mo alloy electrode for welding structural steel.
B. Welding in connection with hardening of soft annealed 1.2363 steel/" target="_blank" class="keylink">tool steel.
· Heat to austenitizing temperature.
· Cool to approx. 500°C.
· Weld at approx. 500°C.
· Cool to approx. 100°C in the same way as at normal hardening, then temper to desired hardness.
Electrode: Hard facing electrode.
C. Repair welding of 1.2363 steel/" target="_blank" class="keylink">tool steel in hardened and tempered condition.
· Preheat to the tempering temperature (min. 200°C) previously used.
· Weld at tempering temperature.
· Heat immediately to tempering temperature, but max. 300°C. Soaking time 3 hours.
· Cool in air to approx. 80°C.
· Heat to tempering temperature. Soaking time 2 hours.
Electrode: Hard facing electrode.
Physical Properties: 1.2363 X100CrMoV5-01 | Temperature: | ||
20°C | 200°C | 400°C | |
Density (Kg/dm³) | 7.75 | 7.70 | 7.65 |
Coefficient of thermal expansion (per °C from 0°C) | - | 11.6 x 10-6 | 11.3 x 10-6 |
Thermal conductivity (cal/cm.s °C) | 62.4 x 10-3 | 64.8 x 10-3 | 68.4 x 10-3 |
Specific heat (cal/g °C) | 0.110 | ||
Modulus of elasticity: | |||
Kp/mm² | 19 370 | 18 900 | 17 325 |
N/mm² | 189 900 | 185 200 | 169 800 |
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.2363 X100CrMoV5-1 Tool Steel round bar 1.2363 X100CrMoV5-1 Tool Steel,forging 1.2363 X100CrMoV5-1 Tool Steel,1.2363 X100CrMoV5-1 Tool Steel sheet,coil 1.2363 X100CrMoV5-1 Tool Steel,1.2363 X100CrMoV5-1 Tool Steel flat bar,pipe 1.2363 X100CrMoV5-1 Tool Steel,1.2363 X100CrMoV5-1 Tool Steel Lrregular