1.2379 X155CrVMo12-1 Tool Steel
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2379 X155CrVMo12-1 Tool Steel
1.2379 X155CrVMo12-1 is a high carbon, high chromium, molybdenum, vanadium, air hardening steel/" target="_blank" class="keylink">tool steel which offershigh surface hardness, good wear resistance, through hardening properties, dimensional stability and high resistance to tempering effect. 1.2379 X155CrVMo12-1 steel/" target="_blank" class="keylink">tool steel is also suitable for vacuum hardening. |
Typical Analysis 1.2379 X155CrVMo12-1 | ||||
C. |
Si. |
Cr. |
Mo. |
V. |
1.50% |
0.30% |
12.00% |
0.80% |
0.90% |
Forging:
Heat slowly and uniformly to 700°C then more rapidly to 900/1040°C. After forging 1.2379 cool slowly.
Annealing:
Anneal at 850°C and slow furnace cool. Hardness after annealing will be approx. 225 brinell.
Hardening:
Pre heat the 1.2379 component slowly to 750/780°C and thoroughly soak. Continue heating to the final hardening temperature of 1000/1030°C and allow the component to be heated through. Quench in oil or cool in air.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperature and hold for at least one hour per inch of total thickness. Double tempering of 1.2379 is recommended to be carried out with intermediate cooling to room temperature.
Tempering °C |
150 |
200 |
250 |
300 |
350 |
400 |
HRc |
62/61 |
61/60 |
60/59 |
57/56 |
56/55 |
56/55 |
Stress Relieving:
If machining operations have been heavy or if the 1.2379 tool has an unbalanced section, remove stresses before hardening by heating up to 700°C, equalise, then cool slowly.
Hard Chromium Plating:
After hard chromium plating tempering of 1.2379 steel/" target="_blank" class="keylink">tool steel is recommended at 180°C for 4 hours to avoid hydrogen embrittlement. Tempering is to be performed immediately after chromium plating.
Welding:
Due to the high risk of crack formation welding of 1.2379 steel/" target="_blank" class="keylink">tool steel should be avoided, if possible. When, howe ver welding is essential, the following serves as a guide:
A. Welding of soft annealed 1.2379 steel/" target="_blank" class="keylink">tool steel.
· Preheat to 300 - 500°C
· Weld at 300-500°C
· Immediately stress relieve
Electrode: Cr-Mo alloy electrode for welding structural steel.
B. Welding in connection with hardening of soft annealed 1.2379 steel/" target="_blank" class="keylink">tool steel.
· Heat to austenitizing temperature.
· Cool to approx. 500°C
· Weld at approx. 500°C
· Cool to approx. 100°C in the same way as at normal hardening, then temper to desired hardness. Double tempering will
reduce the risk of crack formation.
Electrode: Hard facing electrode.
C. Repair welding of 1.2379 steel/" target="_blank" class="keylink">tool steel in hardened and tempered condition.
· Preheat to the tempering temperature (min. 200°C) previously used.
· Weld at tempering temperature
· Heat immediately to tempering temperature, but max. 300°C. Soaking time 2 hours.
Electrode: Hard facing electrode.
Physical Properties: 1.2379 X155CrVMo12-1 | Temperature: | ||
20°C | 200°C | 400°C | |
Density (kg/dm³) | 7.70 | 7.65 | 7.60 |
Coefficient of thermal expansion (per °C from 0°C) | - | 22.0 x 10-6 | 10.8 x 10-6 |
Thermal conductivity (cal/cm.s °C) | 40.9 x 10-3 | 50.4 x 10-3 | 55.2 x 10-3 |
Specific heat (cal/g °C) | 0.110 | ||
Modulus of elasticity: | |||
Kp/mm² | 19 700 | 19 200 | 17 650 |
N/mm² | 193 000 | 188 000 | 173 000 |
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.2379 X155CrVMo12-1 Tool Steel round bar 1.2379 X155CrVMo12-1 Tool Steel,forging 1.2379 X155CrVMo12-1 Tool Steel,1.2379 X155CrVMo12-1 Tool Steel sheet,coil 1.2379 X155CrVMo12-1 Tool Steel,1.2379 X155CrVMo12-1 Tool Steel flat bar,pipe 1.2379 X155CrVMo12-1 Tool Steel,1.2379 X155CrVMo12-1 Tool Steel Lrregular