1.4016, DIN X6Cr17, AISI 430
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.4016, DIN X6Cr17, AISI 430
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
PK336 | 336 | 1.4016 | X6Cr17 | X6Cr17 | 430 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
max. 0.08 | max. 1.00 | max. 1.00 | 17.00 | - | - | - | - | - |
Description
A basic ferritic non-heat treatable stainless steel. Its strengths are in ductility, formability, good corrosion and oxidation resistance, thermal conductivity and finish quality.
Applications
Appliance, automotive and architectural trim, vaults, heat exchangers, scientific apparatus and vending machine components, cuttlery tools, dish washing troughs, buffers, wheel lids, component parts for the soap and petrochemical industry.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 220
Density [g/cm3]: 7.7
Thermal conductivity [W/m.K]: 25.0
Electric resistivity [Ohm mm2/m]: 0.60
Specific heat capacity[J/g.K]: 0.46
Magnetisable: No
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC |
10.0 | 10.0 | 10.5 | 10.5 | 11.0 |
Annealing
Heat to 750-780oC, cool slowly.
Hardening
430 does not respond to hardening by heat treatment.
Mechanical properties at at ambient temperature
Condition: Annealed
Hardness: 185 HB
0.2% proof stress: 270 N/mm2
Tensile strength: 450-600 N/mm2
Elongation: 20% (Longit.)
Forging
Hot forming temperature: 1100-800oC.
Machinability
Rated at 60 % of B1112. Relatively easily machined in all common procedures.
Welding
All common welding methods used for stainless will be successful with 430. Filler metal should be AWS E/ER308 or 312.
Corrosion Resistance
Resistant to fresh water and mild atmospheric corrodants. Successful in exterior automotive trim applications except in coastal areas where salt water and air will cause corrosion.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.4016 DIN X6Cr17 AISI 430 round bar 1.4016, DIN X6Cr17, AISI 430,forging 1.4016, DIN X6Cr17, AISI 430,1.4016, DIN X6Cr17, AISI 430 sheet,coil 1.4016, DIN X6Cr17, AISI 430,1.4016, DIN X6Cr17, AISI 430 flat bar,pipe 1.4016, DIN X6Cr17, AISI 430,1.4016, DIN X6Cr17, AISI 430 Lrregular