- 1.4724, DIN X10CrAl13 round bar
- 1.4724, DIN X10CrAl13 forging
- 1.4724, DIN X10CrAl13 sheet
- 1.4724, DIN X10CrAl13 flat bar
- 1.4724, DIN X10CrAl13 pipe
1.4724, DIN X10CrAl13
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.4724, DIN X10CrAl13
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
PK924 | 924 | 1.4724 | X10CrAl13 | X10CrSiAl13 | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
max. 0.12 | 1.05 | max. 1.00 | 13.00 | - | - | - | - | Al: 0.95 |
Description
Heat resistant stainless steel with excellent corrosion resistance.
Applications
Heat resistant up to temperature up to 850oC, and also can be used in sulphur containing gas. Bearing and conveying components, heat resistant components for thermal boilers, etc.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.7
Thermal conductivity [W/m.K]: 21.0
Electric resistivity [Ohm mm2/m]: 0.90
Specific heat capacity[J/g.K]: 0.45
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-200oC | 20-400oC | 20-600oC | 20-800oC |
11.0 | 11.5 | 12.5 | 13.5 |
Soft Annealing
Heat to 800-850oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 192.
Hardening
Harden from a temperature of 940-980oC followed by oil quenching or warm bath approx. 400oC. Hardness after quenching is 64-66 HRC.
Tempering
Tempering temperature: See the data bellow.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 200oC | 300oC | 400oC | 500oC | 600oC |
64 | 62 | 60 | 57 | 53 | 42 |
Forging
Hot forming temperature: 1100-800oC.
Machinability
Soft and ductile, PK924 can be easily machined using most standard practices. Experienced machinists comment that PK924 machines similarly to 4130 steel/" target="_blank" class="keylink">alloy steel.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.4724 DIN X10CrAl13 round bar 1.4724, DIN X10CrAl13,forging 1.4724, DIN X10CrAl13,1.4724, DIN X10CrAl13 sheet,coil 1.4724, DIN X10CrAl13,1.4724, DIN X10CrAl13 flat bar,pipe 1.4724, DIN X10CrAl13,1.4724, DIN X10CrAl13 Lrregular