1.2208, DIN 31CrV3
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.2208, DIN 31CrV3
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
31CRV3 | 737 | 1.2208 | 31CrV3 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.31 | 0.33 | 0.50 | 0.55 | - | - | 0.10 | - | - |
Description
Cold work steel/" target="_blank" class="keylink">tool steel.
Applications
Steel used for water hardened machine spanners, screw spanners, screwdrivers.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Continuous Cooling Transformation (CCT) Diagram
Time-Temperature Transformation (TTT) Diagram
Soft Annealing
Heat to 680-720oC, cool slowly. This will produce a maximum Brinell hardness of 220.
Hardening
Harden from a temperature of 830-860oC followed by water quenching. Hardness after quenching is 52-55 HRC.
Tempering
Please see the data bellow.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 200oC | 300oC | 400oC |
52 | 50 | 47 | 43 |
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance