1.7103, DIN 67SiCr5, SAE 9254
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.7103, DIN 67SiCr5, SAE 9254
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
PER1 | 714 | 1.7103 | 67SiCr5 | 67SiCr5 | SAE 9254 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.67 | 1.30 | 0.50 | 0.50 | - | - | - | - | - |
Description
Alloyed carbon steel.
Applications
Tap springs, valve springs, ring-shape springs, heat resisting springs.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.82
Continuous Cooling Transformation (CCT) Diagram
Time-Temperature Transformation (TTT) Diagram
Soft Annealing
Heat to 640-680oC, cool slowly. This will produce a maximum Brinell hardness of 255.
Normalizing
Temperature: 850-880oC.
Hardening
Harden from a temperature of 830-860oC followed by oil quenching. Hardness after quenching is min. 54 HRC.
Tempering
Tempering temperature: 350-550oC.
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance
Related hot word search:1.7103 DIN 67SiCr5 SAE 9254 round bar 1.7103, DIN 67SiCr5, SAE 9254,forging 1.7103, DIN 67SiCr5, SAE 9254,1.7103, DIN 67SiCr5, SAE 9254 sheet,coil 1.7103, DIN 67SiCr5, SAE 9254,1.7103, DIN 67SiCr5, SAE 9254 flat bar,pipe 1.7103, DIN 67SiCr5, SAE 9254,1.7103, DIN 67SiCr5, SAE 9254 Lrregular