1.8161, DIN 58CrV4
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.8161, DIN 58CrV4
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
PO186 | 186 | 1.8161 | 58CrV4 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.59 | 0.28 | 0.90 | 1.05 | - | - | 0.15 | - | - |
Description
Alloyed carbon steel, spring steel.
Applications
Quenched and subsequently tempered steel for extremely wear resisting components, driving components, gears.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 680-720oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 248.
Normalizing
Temperature: 850-880oC, air.
Stress Relieving
Temperature: 120-200oC.
Hardening
Harden from a temperature of 820-850oC followed by oil quenching. Hardness after quenching is 60-65 HRC.
Tempering
Tempering temperature: 480-650oC.
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance