1.6773, DIN 36NiCrMo16
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.6773, DIN 36NiCrMo16
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
35NCD16 | 934 | 1.6773 | 36NiCrMo16 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.35 | max. 0.40 | 0.45 | 1.80 | 0.35 | 3.85 | - | - | - |
Description
Structural steel with high strength.
Applications
Structural steel of a broad application range for wear resistant components, exposed to high permanent stress. Due to good hardenability, this steel grade is suitable for lager cross sections, too. It can be used for tools (e.g., cutters) with a hardness of 45-50 HRC.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.80
Soft Annealing
Heat to 650-680oC, cool slowly. This will produce a maximum Brinell hardness of 269.
Normalizing
Temperature: 850-880oC.
Hardening
Harden from a temperature of 835-865oC, 855-885oC followed by oil or quenching.
Tempering
Tempering temperature: 550-650oC.
Mechanical Properties in Quenched and Tempered Condition
Diameter in mm | 0.2 proof stress (N/mm2) | Tensile stregth (N/mm2) | Elongation (%) | Reduction (%) | Impact energy (J) |
Up to 16 | 1050 | 1250-1450 | 9 | 40 | 30 |
17-40 | 1050 | 1250-1450 | 9 | 40 | 30 |
41-100 | 900 | 1100-1300 | 10 | 45 | 35 |
101-160 | 800 | 1000-1200 | 11 | 50 | 45 |
161-250 | 800 | 1000-1200 | 11 | 50 | 45 |
Hardenability Diagram
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance