- 1.7734 EN 15CDV6 round bar
- 1.7734 EN 15CDV6 forging
- 1.7734 EN 15CDV6 sheet
- 1.7734 EN 15CDV6 flat bar
- 1.7734 EN 15CDV6 pipe
1.7734 EN 15CDV6
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.7734
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
PO795 | 795 | 1.7734 | - | 15CDV6 | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.15 | max. 0.20 | 0.95 | 1.38 | 0.90 | - | 0.25 | - | - |
Description
This is chromium-molybdenum-vanadium Structural steels. Good bending performance and excellent weldability. Toughness, consistency and resistance to fatique derived from the high level of micro cleanliness.
Applications
Component parts for the aircraft industry.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 190-210
Density [g/cm3]: 7.80
Continuous Cooling Transformation (CCT) Diagram
Time-Temperature Transformation (TTT) Diagram
Soft Annealing
Please ask.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Quenching temperature: 975oC.
Tempering
Temperature: 600-740oC.
Forging
Hot forming temperature: 1050-850oC.
Machinability
No data.
Mechanical properties
Heat treatment
Machining
Welding performance