Home > Standard > 1.4841, DIN X15CrNiSi25-20, AISI 314 standard

1.4841, DIN X15CrNiSi25-20, AISI 314

1.4841, DIN X15CrNiSi25-20, AISI 314 standard Download, We provide the main countries around the ISO standard download, including: AISI(US),UNS(US),SAE(US),ASTM(US),AMS(US),ASME(US),MIL(US),FED(US),DIN(DEU),JIS(JPN),AFNOR(FR),B.S.(UK),SS(SWE),UNI(ITA).

Production specification

Round bar standard Download
Square-shape steel standard Download
Plate steel standard Download
Billet standard Download
Flat bar standard Download
wire standard Download
tube standard Download
pipe standard Download
Forging standard Download
casting standard Download
sheet standard Download
round bar standard Download
coil standard Download
Bar stock standard Download
profiled bar standard Download

 1.4841, DIN X15CrNiSi25-20, AISI 314

Designation by Standards

 

Brand Name LH No. Mat. No. DIN EN AISI
PK19 920 1.4841 X15CrNiSi25-20 X15CrNiSi2520 314



Chemical Composition (in weight %)

C Si Mn Cr Mo Ni V W Others
max. 0.20 max. 2.00 max. 2.00 25.00 - 20.50 - - -



Description
PK19 is a heat resistant austenitic steel grade characterized by good high temperature strength at elevetaed temperatures. Steel is heat resistant up to to 1000oC. It can thus primarily be used wherever high mechanical stress occour.

Applications
Application examples: grids, fittings, supporting/walking beams, blowers, superheater parts, pipe clips, component parts for furnaces, steam boilers, sheath tubes for thermocouples.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: Approx. 210
Density [g/cm3]: 7.9
Thermal conductivity [W/m.K]: 15, 19 (500oC)
Electric resistivity [Ohm mm2/m]: 0.90
Specific heat capacity[J/g.K]: 0.50
Magnetisable: No

Coefficient of Linear Thermal Expansion 10-6 oC-1

20-200oC 20-400oC 20-600oC 20-800oC 20-1000oC
15.5 17.0 17.5 18.0 19.0



Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Quenching
Harden from a temperature of 1050-1150oC followed by water or air (sufficienty fast) quenching. Structure after quenching is austenite.

Mechanical properties at room temperature in solution-annealed condition
For size range: <=160 mm and solution-annealed condition
Hardnees: Approx. 223 HB
0.2 % proof stress: 230 N/mm2
1.0 % proof stress: 270 N/mm2
Tensile strength: 550-750 N/mm2
Elongation after fracture AT min: 30%

Approximate data on long-term high temperature resistance + AT condition

1% Creep Limit in N/mm2 vs. Temperature in oC

Hours 600oC 700oC 800oC 900oC 1000oC
1 000 105 50 23 10 3
10 000 95 35 10 4 -

Forging
Hot forming temperature: 1150-800oC, cooling in air.

Machinability
This alloy machines similarly to type 304 stainless. Its chips are stringy and it will work harden rapidly. It is necessary to keep the tool cutting at all times and use chip breakers.

Application Temperature: Maximum application temperature in air is 1000oC.

Corrosion Resistance
Steel is resistant to scaling in oxidizing atmospheres at up to 1050oC. Steel is sensitive to SO2, and particularly gases containing H2S at temperatures in excess of 650oC. It is also displays a certain sensitivity to carburising gases, especially at temperatures above 900oC. PK15 displays a tendency towards embrittlement due to Sigma-phase formation during continuous operation in the temperature range between 600 and 850oC.

Welding
Most of the austenitic stainless steels can be readily welded using fusion or resistance methods. Oxyacetylene welding is not recommended. Filler metal should be AWS E/ER 309 or 309L.

Cold working
Although this alloy has a high work hardening rate, it can be drawn, headed, upset, and stamped. Full annealing is required after cold work to remove internal stress.

Related hot word search:1.4841 DIN X15CrNiSi25-20 AISI 314 1.4841, DIN X15CrNiSi25-20, AISI 314 round bar,1.4841, DIN X15CrNiSi25-20, AISI 314 forging,1.4841, DIN X15CrNiSi25-20, AISI 314 sheet,1.4841, DIN X15CrNiSi25-20, AISI 314 coil,1.4841, DIN X15CrNiSi25-20, AISI 314 flat bar,1.4841, DIN X15CrNiSi25-20, AISI 314 pipe,1.4841, DIN X15CrNiSi25-20, AISI 314 Lrregular