1.0601, DIN C60, AISI 1060
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.0601, DIN C60, AISI 1060
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
C60 | 519 | 1.0601 | C60 | - | 1060 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.61 | max. 0.40 | 0.75 | max. 0.40 | max. 0.10 | max. 0.40 | - | - | (Cr+Mo+Ni)= max. 0.63 |
Description
C60 is one of the higher carbon content (0.60%) steels. It is more difficult to fabricate than the lower carbon grades.
Applications
Applications include hand tools such as screwdrivers, pliers and similar items.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m.K]: 46.6
Electric resistivity [Ohm mm2/m]: 0.127
Specific heat capacity[J/g.K]: 0.46
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC |
11.1 | 12.1 | 12.9 | 13.5 | 13.9 |
Soft Annealing
Heat to 680-710oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 241.
Normalizing
Normalizing temperature: 820-860oC/air.
Hardening
Harden from a temperature of 800-840oC followed by water or oil quenching.
Tempering
Tempering temperature: 550-660oC/air.
Mechanical Properties in Hardened+Tempered Condition
Diameter (mm) | 0.2 % proof stress (N/mm2) | Tensile strength (N/mm2) | Elongation A5 (%) | Reduction Z (%) |
up to 16 | 570 | 830-980 | 11 | 20 |
17-40 | 490 | 780-930 | 13 | 30 |
41-100 | 450 | 740-890 | 14 | 35 |
Mechanical Properties in Normalized Condition
Diameter (mm) | 0.2 % proof stress (N/mm2) | Tensile strength (N/mm2) | Elongation A5 (%) |
up to 16 | min. 380 | min. 710 | min. 10 |
17-100 | min. 340 | min. 670 | min. 11 |
101-250 | min. 310 | min. 650 | min. 11 |
Forging
Hot forming temperature: 1100-800oC.
Machinability
Machinability of C60 and all of the higher carbon steels is relatively poor. C60 rates at 55 to 60 % that of the AISI 1112 steel which is considered 100% machinable.
Corrosion Resistance
This steel is not corrosion resistant. it will rust unless protected.
Welding
C60 may be welded by all of the conventional methods. However both pre-heat and post-heat should be used when welding by an approved procedure. Pre-heat at 260 to 320oC and post-heat at 650 to 780oC.
Cold working
Cold working is difficult even in the annealed condition although it may be done by conventional methods but requires greater force than the lower carbon steels.
Mechanical properties
Heat treatment
Machining
Welding performance